Yttria Partially Stabilized Zirconia
Composition
Y2O3 Partially Stabilized ZrO2
yttria partially stabilized zirconia overview
Yttria Partially Stabilized Zirconia (YTZP) components are very strong, and can be employed in extreme environments. This material excels in machinery and mechanical applications requiring corrosion and insulative properties matched with fatigue resistance and impact loading excellence. Additionally, unique mechanical properties allow for an exceptional surface finish on the sub-micron scale.
Example Applications
- Can tooling
- Deep well components
CoorsTek Formulations
Contact a CoorsTek expert to choose a Yttria Partially Stabilized Zirconia solution for your application.
| Property | Units | Value |
|---|---|---|
Flexural Strength, MOR (20 °C) |
MPa |
800-1720 |
Fracture Toughness, KIc |
MPa m1/2 |
6.0-13.0 |
Thermal Conductivity (20 °C) |
W/m K |
2.0-2.2 |
Coefficient of Thermal Expansion |
1 x 10-6/°C |
10.0-10.3 |
Maximum Use Temperature |
°C |
1000-1500 |
Dielectric Strength (6.35mm) |
ac-kV/mm |
9.0 |
Dielectric Loss (tan δ) |
1MHz, 25 °C |
0.001 |
Volume Resistivity (25°C) |
Ω-cm |
1012->1013 |
The information provided on this chart is for general material property reference only. The customer should recognize that exact properties of materials may vary according to product configuration but close control of values of most properties can be maintained, if specified. Nothing herein is provided, or is to be construed, as absolute engineering data or constituting a warranty or representation. Contact CoorsTek for cost-effective design, development and manufacturing assistance. CoorsTek has 300+ variations including various forming and firing processes, not all variants are represented in the present website.